Назва: Retardation of nanoparticles growth by doping
Автори: Nosenko, V.
Rudko, G.
Fediv, V.I.
Savchuk, A.
Gule, E.G.
Vorona, I.
Ключові слова: Doping; Colloidal nanoparticles; CdS; CdS:Mn; Polyvinyl alcohol; Radius size
Дата публікації: 31-бер-2015
Серія/номер: Nanoscale Research Letters;2014, 9:683 http://www.nanoscalereslett.com/content/9/1/683
Короткий огляд (реферат): The process of doping of CdS nanoparticles with Mn during colloidal synthesis is analyzed by EPR and optical studies. Analysis of EPR results demonstrated that Mn2+ ions are successfully incorporated into the nanoparticles and occupy the crystal sites both in the bulk of a NP and near the surface of a NP. Optical absorption measurements revealed the retardation of absorption edge shift during the growth for Mn-doped CdS NPs as compared to the undoped CdS NPs. It was concluded that the presence of Mn in the solution leads to the inhibition of NPs growth.
URI (Уніфікований ідентифікатор ресурсу): http://dspace.bsmu.edu.ua:8080/xmlui/handle/123456789/8465
Розташовується у зібраннях:Статті. Кафедра біологічної фізики та медичної інформатики

Файли цього матеріалу:
Файл Опис РозмірФормат 
Nosenko 2014.pdf465.82 kBAdobe PDFЕскіз
Переглянути/Відкрити


Усі матеріали в архіві електронних ресурсів захищені авторським правом, всі права збережені.